Dehydriding reaction of AlH3: in situ microscopic observations combined with thermal and surface analyses
Ikeda, K
Muto, S
Tatsumi, K
Menjo, M
Kato, S
Bielmann, M
Züttel, A
Jensen, CM
Orimo, S
open access
The dehydriding reaction of single-phase α- AlH3 was investigated by in situ microscopic observations combined with thermal and surface analyses. Before the dehydriding reaction, primary AlH3 particles of size 100 nm–1 µm were thought to be covered by an oxide layer with a thickness of less than 5 nm. Both the precipitation/grain-growth of metallic Al of size 1–50 nm and an increase in 'boundary space' were clearly observed inside the particles, while the morphologies of the particles covered by the layer did not change during the dehydriding reaction. This preliminary report provides fundamental information for a further study of AlH3 as a possible hydrogen storage material.
IOP Publishing
2009-04
eng
journal article
AM
http://hdl.handle.net/2237/20782
https://nagoya.repo.nii.ac.jp/records/18686
https://doi.org/10.1088/0957-4484/20/20/204004
0957-4484
Nanotechnology
20
20
204004
204004
https://nagoya.repo.nii.ac.jp/record/18686/files/Nanotech_AlH3.pdf
application/pdf
729.3 kB
2018-02-21