@article{oai:nagoya.repo.nii.ac.jp:00028209,
 author = {Terao, Yuya and Satoh, Kotaro and Kamigaito, Masami},
 issue = {1},
 journal = {Biomacromolecules},
 month = {Jan},
 note = {A series of cinnamic monomers, which can be derived from naturally occurring phenylpropanoids, were radically copolymerized with vinyl monomers such as methyl acrylate (MA) and styrene (St). Although the monomer reactivity ratios were close to zero for all the cinnamic monomers, such as methyl cinnamate (CAMe), cinnamic acid (CA), N-isopropyl cinnamide (CNIPAm), cinnamaldehyde (CAld), and cinnamonitrile (CN), they were incorporated into the copolymers and significantly increased the glass transition temperatures despite the relatively low incorporation rates of up to 40 mol % due to their rigid 1,2-disubstituted structures. The regioselectivity of the radical copolymerization of CAMe was evaluated on the basis of the results of ruthenium-catalyzed atom transfer radical additions as model reactions. The obtained products suggest that the radicals of MA and St predominantly attack the vinyl carbon of the carbonyl side of CAMe and that the propagation of CAMe mainly occurs via the styrenic radical. The ruthenium-catalyzed living radical polymerization, nitroxide-mediated polymerization (NMP), and reversible addition–fragmentation chain transfer (RAFT) polymerization provided the copolymers with controlled molecular weights, narrow molecular weight distributions, and controlled comonomer compositions. The copolymers of N-isopropylacrylamide (NIPAM) and CNIPAm prepared via RAFT copolymerization showed thermoresponsivity with a lower critical solution temperature (LCST) that could be tuned by altering the comonomer incorporation and a higher LCST than the copolymers of NIPAM and St, which possessed similar molecular weights and similar NIPAM contents, due to the additional N-isopropylamide groups in the CNIPAm units compared to the St units., ファイル公開：2020-01-14},
 pages = {192--203},
 title = {Controlled Radical Copolymerization of Cinnamic Derivatives as Renewable Vinyl Monomers with Both Acrylic and Styrenic Substituents: Reactivity, Regioselectivity, Properties, and Functions},
 volume = {20},
 year = {2019}
}