 note = {This study examined an accelerated corrosion test to examine corrosion degradation of coating systems for steel bridges. Three types of organic coating systems called as A-, C-, and I-painting systems in Japan and four types of metallic coating systems, zinc hop-dip galvanizing, zinc-aluminum alloy spraying by two methods and aluminum spraying, were considered. Scribe circles reaching steel substrate were made mechanically on the coated steel plates, and corrosion from them was focused. Test specimens were exposed to the accelerated corrosion environments conforming to Japanese Industrial Standards K5621 during 300 days for the metal-coated specimens and 400 days for the painted specimens. From the appearance change with passage of testing time, anticorrosive performance of the coating systems was discussed. The corrosion degradation curves for the painted specimens were presented based on blistering area of painting films.},
 pages = {1669--1674},
 title = {An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges},
 volume = {2},
 year = {2005}
}