{"_buckets": {"deposit": "adc37b52-b996-499d-94f4-c03a1d748e7f"}, "_deposit": {"id": "7446", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "7446"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00007446", "sets": ["322"]}, "author_link": ["20840", "20841", "20842", "20843"], "item_10_alternative_title_19": {"attribute_name": "その他のタイトル", "attribute_value_mlt": [{"subitem_alternative_title": "Effect of Stress Ratio on Growth Behavior of Mode III Interlaminar Fatigue Cracks in High Strength GFRP", "subitem_alternative_title_language": "en"}]}, "item_10_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2006-05", "bibliographicIssueDateType": "Issued"}, "bibliographicIssueNumber": "717", "bibliographicPageEnd": "711", "bibliographicPageStart": "704", "bibliographicVolumeNumber": "72", "bibliographic_titles": [{"bibliographic_title": "日本機械学會論文集 A編", "bibliographic_titleLang": "ja"}]}]}, "item_10_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "The mode III crack growth tests were carried out by edge crack torsion specimens under cyclic and monotonic loadings with UD laminates (made of unidirectional laminates) and C laminates (made of unidirectional laminates and cloth laminates) of high strength glass fiber reinforced plastics (GFRP). The test results of mode III crack growth were compared with those of mode Ⅰand II. The fracture toughness, G_IIIR, was nearly constant during the crack extension of about 2 mm for UD and C laminates. The fracture toughness value for UD laminates was much lower than that of C laminates. The fracture toughness increased in the order of model Ⅰ, III, and II. Fatigue crack growth tests were carried out at the stress ratios of R=0.1, -0.5, and -1. In the low growth rate region, the crack growth behavior was controlled by the range of the energy release rate, ΔGm, in UD and C laminates. The threshold value of the range, ΔG_IIIth, was independent of the stress ratio in UD laminate, while, in C laminates, the value of ΔG_IIIth at the negative stress ratio was about 1.6 times larger than at positive stress ratio. In the high growth rate region of UD and C laminates, the crack growth behavior was controlled by the maximum value of the energy release rate, G_IIImax, as in the case of mode II.", "subitem_description_language": "en", "subitem_description_type": "Abstract"}]}, "item_10_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/9127"}]}, "item_10_publisher_32": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "日本機械学会", "subitem_publisher_language": "ja"}]}, "item_10_relation_43": {"attribute_name": "関連情報", "attribute_value_mlt": [{"subitem_relation_type": "isVersionOf", "subitem_relation_type_id": {"subitem_relation_type_id_text": "http://ci.nii.ac.jp/naid/110004731584/", "subitem_relation_type_select": "URI"}}]}, "item_10_rights_12": {"attribute_name": "権利", "attribute_value_mlt": [{"subitem_rights": "日本機械学会", "subitem_rights_language": "ja"}, {"subitem_rights": "本文データは学協会の許諾に基づきCiNiiから複製したものである。", "subitem_rights_language": "ja"}]}, "item_10_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_10_source_id_7": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "0387-5008", "subitem_source_identifier_type": "PISSN"}]}, "item_10_text_14": {"attribute_name": "フォーマット", "attribute_value_mlt": [{"subitem_text_value": "application/pdf"}]}, "item_1615787544753": {"attribute_name": "出版タイプ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "松原, 剛", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "20840", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "MATSUBARA, Go", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "20841", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "田中, 啓介", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "20842", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "TANAKA, Keisuke", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "20843", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-19"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "JsMecEngA_72-717-704.pdf", "filesize": [{"value": "799.3 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 799300.0, "url": {"label": "JsMecEngA_72-717-704.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/7446/files/JsMecEngA_72-717-704.pdf"}, "version_id": "de7256f7-7528-4e7e-92f1-3ab03085f26d"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Mode III", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Fatigue", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Delamination", "subitem_subject_scheme": "Other"}, {"subitem_subject": "GFRP", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Stress Ratio", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Energy Release Rate", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Crack Propagation", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Interlaminar Shear", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Composite Material", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "高強度GFRPのモードIII層間はく離疲労き裂進展におよぼす応力比の影響", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "高強度GFRPのモードIII層間はく離疲労き裂進展におよぼす応力比の影響", "subitem_title_language": "ja"}]}, "item_type_id": "10", "owner": "1", "path": ["322"], "permalink_uri": "http://hdl.handle.net/2237/9127", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2007-12-11"}, "publish_date": "2007-12-11", "publish_status": "0", "recid": "7446", "relation": {}, "relation_version_is_last": true, "title": ["高強度GFRPのモードIII層間はく離疲労き裂進展におよぼす応力比の影響"], "weko_shared_id": -1}
高強度GFRPのモードIII層間はく離疲労き裂進展におよぼす応力比の影響
http://hdl.handle.net/2237/9127
http://hdl.handle.net/2237/91279982a0fa-b0fb-4b1d-9fbf-22ed43388b94
名前 / ファイル | ライセンス | アクション |
---|---|---|
![]() |
|
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2007-12-11 | |||||
タイトル | ||||||
タイトル | 高強度GFRPのモードIII層間はく離疲労き裂進展におよぼす応力比の影響 | |||||
言語 | ja | |||||
その他のタイトル | ||||||
その他のタイトル | Effect of Stress Ratio on Growth Behavior of Mode III Interlaminar Fatigue Cracks in High Strength GFRP | |||||
言語 | en | |||||
著者 |
松原, 剛
× 松原, 剛× MATSUBARA, Go× 田中, 啓介× TANAKA, Keisuke |
|||||
アクセス権 | ||||||
アクセス権 | open access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
権利 | ||||||
言語 | ja | |||||
権利情報 | 日本機械学会 | |||||
権利 | ||||||
言語 | ja | |||||
権利情報 | 本文データは学協会の許諾に基づきCiNiiから複製したものである。 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Mode III | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Fatigue | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Delamination | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | GFRP | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Stress Ratio | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Energy Release Rate | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Crack Propagation | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Interlaminar Shear | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Composite Material | |||||
抄録 | ||||||
内容記述 | The mode III crack growth tests were carried out by edge crack torsion specimens under cyclic and monotonic loadings with UD laminates (made of unidirectional laminates) and C laminates (made of unidirectional laminates and cloth laminates) of high strength glass fiber reinforced plastics (GFRP). The test results of mode III crack growth were compared with those of mode Ⅰand II. The fracture toughness, G_IIIR, was nearly constant during the crack extension of about 2 mm for UD and C laminates. The fracture toughness value for UD laminates was much lower than that of C laminates. The fracture toughness increased in the order of model Ⅰ, III, and II. Fatigue crack growth tests were carried out at the stress ratios of R=0.1, -0.5, and -1. In the low growth rate region, the crack growth behavior was controlled by the range of the energy release rate, ΔGm, in UD and C laminates. The threshold value of the range, ΔG_IIIth, was independent of the stress ratio in UD laminate, while, in C laminates, the value of ΔG_IIIth at the negative stress ratio was about 1.6 times larger than at positive stress ratio. In the high growth rate region of UD and C laminates, the crack growth behavior was controlled by the maximum value of the energy release rate, G_IIImax, as in the case of mode II. | |||||
言語 | en | |||||
内容記述タイプ | Abstract | |||||
出版者 | ||||||
言語 | ja | |||||
出版者 | 日本機械学会 | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源タイプresource | http://purl.org/coar/resource_type/c_6501 | |||||
タイプ | journal article | |||||
出版タイプ | ||||||
出版タイプ | VoR | |||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
関連情報 | ||||||
関連タイプ | isVersionOf | |||||
識別子タイプ | URI | |||||
関連識別子 | http://ci.nii.ac.jp/naid/110004731584/ | |||||
ISSN | ||||||
収録物識別子タイプ | PISSN | |||||
収録物識別子 | 0387-5008 | |||||
書誌情報 |
ja : 日本機械学會論文集 A編 巻 72, 号 717, p. 704-711, 発行日 2006-05 |
|||||
フォーマット | ||||||
application/pdf | ||||||
著者版フラグ | ||||||
値 | publisher | |||||
URI | ||||||
識別子 | http://hdl.handle.net/2237/9127 | |||||
識別子タイプ | HDL |