{"_buckets": {"deposit": "1d1b4992-82eb-4ddb-a53e-01963f4c68ed"}, "_deposit": {"id": "11214", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "11214"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00011214", "sets": ["1093"]}, "author_link": ["33940", "33941", "33942"], "item_1618209983323": {"attribute_name": "助成情報", "attribute_value_mlt": [{"subitem_award_numbers": {"subitem_award_number": "09450047", "subitem_award_uri": "https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-09450047"}, "subitem_award_titles": [{"subitem_award_title": "金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究", "subitem_award_title_language": "ja"}], "subitem_funder_identifiers": {"subitem_funder_identifier": "https://doi.org/10.13039/501100001691", "subitem_funder_identifier_type": "Crossref Funder"}, "subitem_funder_names": [{"subitem_funder_name": "日本学術振興会", "subitem_funder_name_language": "ja"}]}]}, "item_19_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2000-03", "bibliographicIssueDateType": "Issued"}}]}, "item_19_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "1.電子顕微鏡内(SEM)での疲労試験を行い,き裂の発生および進展挙動のその場観察を可能とするシステムを構築した.炭化ケイ素粒子強化複合材料の疲労におけるき裂の主な発生個所は,粒子径約30μmの複合材料では粒子割れであり3μmの場合では母相であることを示し,かつき裂進展過程において微細粒子はき裂進展阻止効果を持つのに対し,30μmの粗大粒の場合は,粒子が割れて加速効果を持つことを明らかにした. 2.有限要素法によるき裂と粒子の相互作用のメゾメカニックス解析をもとにして求めたき裂伝ぱ速度およびき裂の屈曲角き裂の予測が,実験結果と一致することを示し,計算機シミュレーションの道を拓いた. 3.微視組織学的微小き裂の停留条件は,き裂先端からの一本転位の射出条件および逆負荷における転位の消滅条件で与えた.き裂の進展過程での粒界とき裂の相互作用は,連続分布転位論をもとに構築した.ついで,このモデルに塑性誘起き裂閉口の効果を重畳させ,き裂進展のシミュレーションプログラムを開発した.また,力学的微小き裂の挙動は,き裂閉口の形成をもとにしたき裂進展抵抗曲線法(R曲線法)によって予測した. 4.炭化ケイ素粒子およびウイスカで強化されたアルミニウム合金の平滑材の疲労限度,長いき裂の下限界応力拡大係数範囲,下限界有効応力拡大係数範囲に関する従来の報告データを集め,引張り強さとの関係を明らかにした.これらの関数を,き裂停留の機構をもとに検討した.", "subitem_description_language": "ja", "subitem_description_type": "Abstract"}]}, "item_19_description_5": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "科学研究費補助金 研究種目:基盤研究(B)(2) 課題番号:09450047 研究代表者:田中 啓介 研究期間:1997-1999年度", "subitem_description_language": "ja", "subitem_description_type": "Other"}]}, "item_19_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/13086"}]}, "item_19_relation_40": {"attribute_name": "シリーズ", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "科学研究費補助金報告書;基盤研究(B)(2);09450047"}]}]}, "item_19_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_19_text_14": {"attribute_name": "フォーマット", "attribute_value_mlt": [{"subitem_text_value": "application/pdf"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "田中, 啓介", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "33940", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "秋庭, 義明", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "33941", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "田中, 拓", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "33942", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-20"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "09450047.pdf", "filesize": [{"value": "9.9 MB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 9900000.0, "url": {"label": "09450047.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/11214/files/09450047.pdf"}, "version_id": "55041da3-5784-4b66-b438-ef0f7c11ba27"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Crack closure", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Crack propagation", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Fatigue", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Fracture mechanics", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Mesomechanics", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Metal matrix Composite", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Residual stress", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Small crack", "subitem_subject_scheme": "Other"}, {"subitem_subject": "き裂伝ば", "subitem_subject_scheme": "Other"}, {"subitem_subject": "き裂伝ぱ", "subitem_subject_scheme": "Other"}, {"subitem_subject": "き裂閉口", "subitem_subject_scheme": "Other"}, {"subitem_subject": "メゾメカニックス", "subitem_subject_scheme": "Other"}, {"subitem_subject": "微小き裂", "subitem_subject_scheme": "Other"}, {"subitem_subject": "残留応力", "subitem_subject_scheme": "Other"}, {"subitem_subject": "疲労", "subitem_subject_scheme": "Other"}, {"subitem_subject": "破壊力学", "subitem_subject_scheme": "Other"}, {"subitem_subject": "金属基複合材料", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "research report", "resourceuri": "http://purl.org/coar/resource_type/c_18ws"}]}, "item_title": "金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究", "subitem_title_language": "ja"}]}, "item_type_id": "19", "owner": "1", "path": ["1093"], "permalink_uri": "http://hdl.handle.net/2237/13086", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2010-04-07"}, "publish_date": "2010-04-07", "publish_status": "0", "recid": "11214", "relation": {}, "relation_version_is_last": true, "title": ["金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究"], "weko_shared_id": -1}
金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究
http://hdl.handle.net/2237/13086
http://hdl.handle.net/2237/130869a224a78-c5b3-4a55-80a3-fc6fe1d0fdce
名前 / ファイル | ライセンス | アクション |
---|---|---|
09450047.pdf (9.9 MB)
|
|
Item type | 研究報告書 / Research Paper(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2010-04-07 | |||||
タイトル | ||||||
タイトル | 金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究 | |||||
言語 | ja | |||||
著者 |
田中, 啓介
× 田中, 啓介× 秋庭, 義明× 田中, 拓 |
|||||
アクセス権 | ||||||
アクセス権 | open access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Crack closure | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Crack propagation | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Fatigue | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Fracture mechanics | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Mesomechanics | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Metal matrix Composite | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Residual stress | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Small crack | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | き裂伝ば | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | き裂伝ぱ | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | き裂閉口 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | メゾメカニックス | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 微小き裂 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 残留応力 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 疲労 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 破壊力学 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 金属基複合材料 | |||||
抄録 | ||||||
内容記述 | 1.電子顕微鏡内(SEM)での疲労試験を行い,き裂の発生および進展挙動のその場観察を可能とするシステムを構築した.炭化ケイ素粒子強化複合材料の疲労におけるき裂の主な発生個所は,粒子径約30μmの複合材料では粒子割れであり3μmの場合では母相であることを示し,かつき裂進展過程において微細粒子はき裂進展阻止効果を持つのに対し,30μmの粗大粒の場合は,粒子が割れて加速効果を持つことを明らかにした. 2.有限要素法によるき裂と粒子の相互作用のメゾメカニックス解析をもとにして求めたき裂伝ぱ速度およびき裂の屈曲角き裂の予測が,実験結果と一致することを示し,計算機シミュレーションの道を拓いた. 3.微視組織学的微小き裂の停留条件は,き裂先端からの一本転位の射出条件および逆負荷における転位の消滅条件で与えた.き裂の進展過程での粒界とき裂の相互作用は,連続分布転位論をもとに構築した.ついで,このモデルに塑性誘起き裂閉口の効果を重畳させ,き裂進展のシミュレーションプログラムを開発した.また,力学的微小き裂の挙動は,き裂閉口の形成をもとにしたき裂進展抵抗曲線法(R曲線法)によって予測した. 4.炭化ケイ素粒子およびウイスカで強化されたアルミニウム合金の平滑材の疲労限度,長いき裂の下限界応力拡大係数範囲,下限界有効応力拡大係数範囲に関する従来の報告データを集め,引張り強さとの関係を明らかにした.これらの関数を,き裂停留の機構をもとに検討した. | |||||
言語 | ja | |||||
内容記述タイプ | Abstract | |||||
内容記述 | ||||||
内容記述 | 科学研究費補助金 研究種目:基盤研究(B)(2) 課題番号:09450047 研究代表者:田中 啓介 研究期間:1997-1999年度 | |||||
言語 | ja | |||||
内容記述タイプ | Other | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源 | http://purl.org/coar/resource_type/c_18ws | |||||
タイプ | research report | |||||
助成情報 | ||||||
識別子タイプ | Crossref Funder | |||||
助成機関識別子 | https://doi.org/10.13039/501100001691 | |||||
助成機関名 | 日本学術振興会 | |||||
言語 | ja | |||||
研究課題番号URI | https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-09450047 | |||||
研究課題番号 | 09450047 | |||||
研究課題名 | 金属基複合材料における微小氷疲労き裂の発生と伝ぱのメゾメカニックス的研究 | |||||
言語 | ja | |||||
書誌情報 |
発行日 2000-03 |
|||||
フォーマット | ||||||
application/pdf | ||||||
著者版フラグ | ||||||
値 | publisher | |||||
シリーズ | ||||||
関連名称 | 科学研究費補助金報告書;基盤研究(B)(2);09450047 | |||||
URI | ||||||
識別子 | http://hdl.handle.net/2237/13086 | |||||
識別子タイプ | HDL |