{"_buckets": {"deposit": "0eb49494-c753-4a55-9000-c126e4889ec9"}, "_deposit": {"id": "16846", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "16846"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00016846", "sets": ["503"]}, "author_link": ["50105", "50106", "50107", "50108"], "item_1615789909678": {"attribute_name": "出版タイプ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_18_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2013-09", "bibliographicIssueDateType": "Issued"}}]}, "item_18_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "A series of accelerated exposure tests with combined cycles during 300 days was carried out for investigating the basic corrosion characteristics of the Sn-bearing steel with paint coating. When noting the specimens with paint systems used for mild corrosion conditions, the blister of the painting from the cross scribe of the Sn-bearing steel was smaller than that of the general structural steel. In the case of the specimens with paint systems used for severe corrosion conditions, almost no blister of the painting from the cross scribe could be observed on the Sn-bearing steel even though the experiment was finished. The blister area from the boundary region between the painting and the steel substrate of the Sn-bearing steel was smaller than that of the SM490 steel. The results indicated the possibility for reducing the cost for maintenance of steel bridges by prolonging repair terms of painting by using the Sn-bearing steel.", "subitem_description_language": "en", "subitem_description_type": "Abstract"}]}, "item_18_description_5": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "The Thirteenth East Asia-Pacific Conference on Structural Engineering and Construction, September 11-13, 2013, Sapporo, Japan (EASEC-13)", "subitem_description_language": "en", "subitem_description_type": "Other"}]}, "item_18_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/18867"}]}, "item_18_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "MORI, T.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50105", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "HIROHATA, M.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50106", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "KAMIMURA, T.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50107", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "ITOH, Y.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50108", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-20"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "B-141.pdf", "filesize": [{"value": "681.4 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 681400.0, "url": {"label": "B-141.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/16846/files/B-141.pdf"}, "version_id": "49ec578e-6f3f-4634-b322-5c90b15a34f9"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Steel structure", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Sn-bearing steel", "subitem_subject_scheme": "Other"}, {"subitem_subject": "corrosion", "subitem_subject_scheme": "Other"}, {"subitem_subject": "paint coating", "subitem_subject_scheme": "Other"}, {"subitem_subject": "accelerated exposure test", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "conference paper", "resourceuri": "http://purl.org/coar/resource_type/c_5794"}]}, "item_title": "DETERIORATION CHARACTERISTICS OF Sn-BEARING STEEL BY ACCELERATED EXPOSURE TESTS", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "DETERIORATION CHARACTERISTICS OF Sn-BEARING STEEL BY ACCELERATED EXPOSURE TESTS", "subitem_title_language": "en"}]}, "item_type_id": "18", "owner": "1", "path": ["503"], "permalink_uri": "http://hdl.handle.net/2237/18867", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2013-11-11"}, "publish_date": "2013-11-11", "publish_status": "0", "recid": "16846", "relation": {}, "relation_version_is_last": true, "title": ["DETERIORATION CHARACTERISTICS OF Sn-BEARING STEEL BY ACCELERATED EXPOSURE TESTS"], "weko_shared_id": -1}
  1. B200 工学部/工学研究科
  2. B200e 会議資料
  3. 国際会議

DETERIORATION CHARACTERISTICS OF Sn-BEARING STEEL BY ACCELERATED EXPOSURE TESTS

http://hdl.handle.net/2237/18867
http://hdl.handle.net/2237/18867
a1d57b1d-e0e8-4ba1-bf5a-221272fa3c42
名前 / ファイル ライセンス アクション
B-141.pdf B-141.pdf (681.4 kB)
Item type 会議発表論文 / Conference Paper(1)
公開日 2013-11-11
タイトル
タイトル DETERIORATION CHARACTERISTICS OF Sn-BEARING STEEL BY ACCELERATED EXPOSURE TESTS
言語 en
著者 MORI, T.

× MORI, T.

WEKO 50105

en MORI, T.

Search repository
HIROHATA, M.

× HIROHATA, M.

WEKO 50106

en HIROHATA, M.

Search repository
KAMIMURA, T.

× KAMIMURA, T.

WEKO 50107

en KAMIMURA, T.

Search repository
ITOH, Y.

× ITOH, Y.

WEKO 50108

en ITOH, Y.

Search repository
アクセス権
アクセス権 open access
アクセス権URI http://purl.org/coar/access_right/c_abf2
キーワード
主題Scheme Other
主題 Steel structure
キーワード
主題Scheme Other
主題 Sn-bearing steel
キーワード
主題Scheme Other
主題 corrosion
キーワード
主題Scheme Other
主題 paint coating
キーワード
主題Scheme Other
主題 accelerated exposure test
抄録
内容記述 A series of accelerated exposure tests with combined cycles during 300 days was carried out for investigating the basic corrosion characteristics of the Sn-bearing steel with paint coating. When noting the specimens with paint systems used for mild corrosion conditions, the blister of the painting from the cross scribe of the Sn-bearing steel was smaller than that of the general structural steel. In the case of the specimens with paint systems used for severe corrosion conditions, almost no blister of the painting from the cross scribe could be observed on the Sn-bearing steel even though the experiment was finished. The blister area from the boundary region between the painting and the steel substrate of the Sn-bearing steel was smaller than that of the SM490 steel. The results indicated the possibility for reducing the cost for maintenance of steel bridges by prolonging repair terms of painting by using the Sn-bearing steel.
言語 en
内容記述タイプ Abstract
内容記述
内容記述 The Thirteenth East Asia-Pacific Conference on Structural Engineering and Construction, September 11-13, 2013, Sapporo, Japan (EASEC-13)
言語 en
内容記述タイプ Other
言語
言語 eng
資源タイプ
資源 http://purl.org/coar/resource_type/c_5794
タイプ conference paper
出版タイプ
出版タイプ VoR
出版タイプResource http://purl.org/coar/version/c_970fb48d4fbd8a85
書誌情報
発行日 2013-09
著者版フラグ
値 publisher
URI
識別子 http://hdl.handle.net/2237/18867
識別子タイプ HDL
戻る
0
views
See details
Views

Versions

Ver.1 2021-03-01 17:23:00.110641
Show All versions

Share

Mendeley Twitter Facebook Print Addthis

Cite as

エクスポート

OAI-PMH
  • OAI-PMH JPCOAR
  • OAI-PMH DublinCore
  • OAI-PMH DDI
Other Formats
  • JSON
  • BIBTEX

Confirm


Powered by WEKO3


Powered by WEKO3