{"_buckets": {"deposit": "226edc38-1d73-4732-aba9-5abfa77ae0f6"}, "_deposit": {"id": "16856", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "16856"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00016856", "sets": ["503"]}, "author_link": ["50136", "50137"], "item_1615789909678": {"attribute_name": "出版タイプ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_18_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2013-07", "bibliographicIssueDateType": "Issued"}, "bibliographic_titles": [{"bibliographic_title": "Proceeding of the 9th Japan-Korea Joint Seminar on Bridge Maintenance July 24-27, 2013, Hokkaido Japan", "bibliographic_titleLang": "en"}]}]}, "item_18_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "In order to examine the corrosion behavior of the welded part of structural steel, the accelerated exposure test with combined system of salt water spray cycles was conducted. The corrosion depths of general part of base metal and welded parts such as the weld toe and the top of weld bead were compared after 800 cycles of the test. The corrosion depths of welded parts were around 54% of that of base metal. The reason was possibly the lower carbon content in the weld metal compared with the base metal. It might be that the corrosion of welded part under this test condition was affected by the material properties rather than the geometric shape of weld bead.", "subitem_description_language": "en", "subitem_description_type": "Abstract"}]}, "item_18_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/18877"}]}, "item_18_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "HIROHATA, Mikihito", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50136", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "ITOH, Yoshito", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "50137", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-20"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "B-139.pdf", "filesize": [{"value": "433.8 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 433800.0, "url": {"label": "B-139.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/16856/files/B-139.pdf"}, "version_id": "89543779-29da-491b-a436-3efe20a1b0af"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Maintenance", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Structural steel", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Corrosion", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Welded part", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Accelerated exposure test", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "conference paper", "resourceuri": "http://purl.org/coar/resource_type/c_5794"}]}, "item_title": "CORROSION BEHAVIOR OF WELDED PART OF STRUCTURAL STEEL BY ACCELERATED EXPOSURE TEST", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "CORROSION BEHAVIOR OF WELDED PART OF STRUCTURAL STEEL BY ACCELERATED EXPOSURE TEST", "subitem_title_language": "en"}]}, "item_type_id": "18", "owner": "1", "path": ["503"], "permalink_uri": "http://hdl.handle.net/2237/18877", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2013-11-13"}, "publish_date": "2013-11-13", "publish_status": "0", "recid": "16856", "relation": {}, "relation_version_is_last": true, "title": ["CORROSION BEHAVIOR OF WELDED PART OF STRUCTURAL STEEL BY ACCELERATED EXPOSURE TEST"], "weko_shared_id": -1}
CORROSION BEHAVIOR OF WELDED PART OF STRUCTURAL STEEL BY ACCELERATED EXPOSURE TEST
http://hdl.handle.net/2237/18877
http://hdl.handle.net/2237/188776b044f17-8f87-4396-9093-96de790b6078
名前 / ファイル | ライセンス | アクション |
---|---|---|
B-139.pdf (433.8 kB)
|
|
Item type | 会議発表論文 / Conference Paper(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2013-11-13 | |||||
タイトル | ||||||
タイトル | CORROSION BEHAVIOR OF WELDED PART OF STRUCTURAL STEEL BY ACCELERATED EXPOSURE TEST | |||||
言語 | en | |||||
著者 |
HIROHATA, Mikihito
× HIROHATA, Mikihito× ITOH, Yoshito |
|||||
アクセス権 | ||||||
アクセス権 | open access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Maintenance | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Structural steel | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Corrosion | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Welded part | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Accelerated exposure test | |||||
抄録 | ||||||
内容記述 | In order to examine the corrosion behavior of the welded part of structural steel, the accelerated exposure test with combined system of salt water spray cycles was conducted. The corrosion depths of general part of base metal and welded parts such as the weld toe and the top of weld bead were compared after 800 cycles of the test. The corrosion depths of welded parts were around 54% of that of base metal. The reason was possibly the lower carbon content in the weld metal compared with the base metal. It might be that the corrosion of welded part under this test condition was affected by the material properties rather than the geometric shape of weld bead. | |||||
言語 | en | |||||
内容記述タイプ | Abstract | |||||
言語 | ||||||
言語 | eng | |||||
資源タイプ | ||||||
資源 | http://purl.org/coar/resource_type/c_5794 | |||||
タイプ | conference paper | |||||
出版タイプ | ||||||
出版タイプ | VoR | |||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
書誌情報 |
en : Proceeding of the 9th Japan-Korea Joint Seminar on Bridge Maintenance July 24-27, 2013, Hokkaido Japan 発行日 2013-07 |
|||||
著者版フラグ | ||||||
値 | publisher | |||||
URI | ||||||
識別子 | http://hdl.handle.net/2237/18877 | |||||
識別子タイプ | HDL |