{"_buckets": {"deposit": "0d850226-edfc-4105-9bc3-bb30d9fdf308"}, "_deposit": {"id": "23880", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "23880"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00023880", "sets": ["503"]}, "author_link": ["70913", "70914", "70915", "70916"], "item_1615789909678": {"attribute_name": "出版タイプ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_18_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2015-05", "bibliographicIssueDateType": "Issued"}}]}, "item_18_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "The steel with a small amount of tin (Sn), that is, Sn-bearing steel was newly developed by noting the effect of adding such kind of trace alloy element for improving the corrosion resistance of steel. In order to investigate the corrosion deterioration characteristics around paint coating defect of the Sn-bearing steel, accelerated exposure test was performed. After the test, the appearance and surface shape of paint coated Sn-bearing steel were examined for evaluating the degree of deterioration. The corrosion deterioration was evaluated by focusing on the blister of paint coating around the initial defect scribed in X shape (namely, cross-scribe defect). The blister areas from the cross scribe paint defect of the Sn-bearing steel was respectively 95 %, in A-type coating and 43 % in C-type coating of those of the SM490 steel at 2200 cycles. For C-type coating, the use of Sn-bearing steel to bridges has the possibility to prolong the life span of paint coating by around 15 %.", "subitem_description_language": "en", "subitem_description_type": "Abstract"}]}, "item_18_description_5": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "Elegance in Structures IABSE Conference, Nara, Japan (May 13-15, 2015, Nara Prefectural New Public Hall in Nara, Japan) NM-11", "subitem_description_language": "en", "subitem_description_type": "Other"}]}, "item_18_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/26074"}]}, "item_18_publisher_32": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "IABSE", "subitem_publisher_language": "en"}]}, "item_18_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "OKUNO, Takafumi", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "70913", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "HIROHATA, Mikihito", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "70914", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "KAMIMURA, Takayuki", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "70915", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "ITOH, Yoshito", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "70916", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-22"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "2-1.pdf", "filesize": [{"value": "1.5 MB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 1500000.0, "url": {"label": "2-1.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/23880/files/2-1.pdf"}, "version_id": "f09e5fbd-b0b6-4247-bce2-82b1c867e664"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "steel bridge", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Sn-bearing steel", "subitem_subject_scheme": "Other"}, {"subitem_subject": "corrosion", "subitem_subject_scheme": "Other"}, {"subitem_subject": "paint coating", "subitem_subject_scheme": "Other"}, {"subitem_subject": "accelerated exposure test", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "conference paper", "resourceuri": "http://purl.org/coar/resource_type/c_5794"}]}, "item_title": "Corrosion deterioration characteristics of Sn-bearing steel and its applicability on steel bridges", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Corrosion deterioration characteristics of Sn-bearing steel and its applicability on steel bridges", "subitem_title_language": "en"}]}, "item_type_id": "18", "owner": "1", "path": ["503"], "permalink_uri": "http://hdl.handle.net/2237/26074", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2017-04-20"}, "publish_date": "2017-04-20", "publish_status": "0", "recid": "23880", "relation": {}, "relation_version_is_last": true, "title": ["Corrosion deterioration characteristics of Sn-bearing steel and its applicability on steel bridges"], "weko_shared_id": -1}
  1. B200 工学部/工学研究科
  2. B200e 会議資料
  3. 国際会議

Corrosion deterioration characteristics of Sn-bearing steel and its applicability on steel bridges

http://hdl.handle.net/2237/26074
http://hdl.handle.net/2237/26074
e4cd95a4-838f-4068-bb68-b9f27c675bde
名前 / ファイル ライセンス アクション
2-1.pdf 2-1.pdf (1.5 MB)
Item type 会議発表論文 / Conference Paper(1)
公開日 2017-04-20
タイトル
タイトル Corrosion deterioration characteristics of Sn-bearing steel and its applicability on steel bridges
言語 en
著者 OKUNO, Takafumi

× OKUNO, Takafumi

WEKO 70913

en OKUNO, Takafumi

Search repository
HIROHATA, Mikihito

× HIROHATA, Mikihito

WEKO 70914

en HIROHATA, Mikihito

Search repository
KAMIMURA, Takayuki

× KAMIMURA, Takayuki

WEKO 70915

en KAMIMURA, Takayuki

Search repository
ITOH, Yoshito

× ITOH, Yoshito

WEKO 70916

en ITOH, Yoshito

Search repository
アクセス権
アクセス権 open access
アクセス権URI http://purl.org/coar/access_right/c_abf2
キーワード
主題Scheme Other
主題 steel bridge
キーワード
主題Scheme Other
主題 Sn-bearing steel
キーワード
主題Scheme Other
主題 corrosion
キーワード
主題Scheme Other
主題 paint coating
キーワード
主題Scheme Other
主題 accelerated exposure test
抄録
内容記述 The steel with a small amount of tin (Sn), that is, Sn-bearing steel was newly developed by noting the effect of adding such kind of trace alloy element for improving the corrosion resistance of steel. In order to investigate the corrosion deterioration characteristics around paint coating defect of the Sn-bearing steel, accelerated exposure test was performed. After the test, the appearance and surface shape of paint coated Sn-bearing steel were examined for evaluating the degree of deterioration. The corrosion deterioration was evaluated by focusing on the blister of paint coating around the initial defect scribed in X shape (namely, cross-scribe defect). The blister areas from the cross scribe paint defect of the Sn-bearing steel was respectively 95 %, in A-type coating and 43 % in C-type coating of those of the SM490 steel at 2200 cycles. For C-type coating, the use of Sn-bearing steel to bridges has the possibility to prolong the life span of paint coating by around 15 %.
言語 en
内容記述タイプ Abstract
内容記述
内容記述 Elegance in Structures IABSE Conference, Nara, Japan (May 13-15, 2015, Nara Prefectural New Public Hall in Nara, Japan) NM-11
言語 en
内容記述タイプ Other
出版者
言語 en
出版者 IABSE
言語
言語 eng
資源タイプ
資源 http://purl.org/coar/resource_type/c_5794
タイプ conference paper
出版タイプ
出版タイプ VoR
出版タイプResource http://purl.org/coar/version/c_970fb48d4fbd8a85
書誌情報
発行日 2015-05
著者版フラグ
値 publisher
URI
識別子 http://hdl.handle.net/2237/26074
識別子タイプ HDL
戻る
0
views
See details
Views

Versions

Ver.1 2021-03-01 14:21:58.176233
Show All versions

Share

Mendeley Twitter Facebook Print Addthis

Cite as

エクスポート

OAI-PMH
  • OAI-PMH JPCOAR
  • OAI-PMH DublinCore
  • OAI-PMH DDI
Other Formats
  • JSON
  • BIBTEX

Confirm


Powered by WEKO3


Powered by WEKO3