環境促進実験を用いた鋼橋塗装系の腐食劣化評価
http://hdl.handle.net/2237/7469
http://hdl.handle.net/2237/746966fd82b3-ddfe-472c-a6fb-34a82fe7b77a
名前 / ファイル | ライセンス | アクション |
---|---|---|
kozo_52A_803.pdf (1.8 MB)
|
|
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2007-03-15 | |||||
タイトル | ||||||
タイトル | 環境促進実験を用いた鋼橋塗装系の腐食劣化評価 | |||||
言語 | ja | |||||
その他のタイトル | ||||||
その他のタイトル | Accelerated corrosion tests for evaluating corrosion degradation of steel bridge painting systems | |||||
言語 | en | |||||
著者 |
金, 仁泰
× 金, 仁泰× Kim, In-Tae× 伊藤, 義人× Itoh, Yoshito× 肥田, 達久× Hida, Tatsuhisa× 小山, 明久× Koyama, Akihisa× 忽那, 幸浩× Kutsuna, Yukihiro |
|||||
アクセス権 | ||||||
アクセス権 | open access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
権利 | ||||||
言語 | ja | |||||
権利情報 | 土木学会 (許諾No.2007-012) | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Steel bridge | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | corrosion | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | accelerated corrosion test | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | painting | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | corrosion degradation | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 鋼橋 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 腐食 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 腐食促進実験 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 塗装 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 腐食耐久性 | |||||
抄録 | ||||||
内容記述 | This study examined to evaluate the corrosion durability of painting systems for steel bridges. Accelerated corrosion cyclic tests conforming to JIS K5621 were carried out on three types of the painting systems, i.e. A-painting system for mild condition, C-painting system for severe corrosion condition, and a newly developed heavy duty I-painting system. Cross-scribed lines reaching the steel substrate were mechanically made in the painted surface, and uncoated region of 20 × 70 mm was also introduced in the lower part of the test specimens. The three types of painted specimens were exposed into the S6-cycle corrosion environments during 100, 200 and 400 days. Blistering area, tensile adhesion, glossiness, appearance and surface geometry of the paintings were measured at the exposure times of 0, 100, 200, 300, and 400 days. After removing painting films and corrosion productions by chemical treatment, the thickness loss of steel substrate was also measured. From the test results, the corrosion degradation degree of the three types of bridge paintings systems was quantiatively evaluated. | |||||
言語 | en | |||||
内容記述タイプ | Abstract | |||||
出版者 | ||||||
言語 | ja | |||||
出版者 | 土木学会 | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源タイプresource | http://purl.org/coar/resource_type/c_6501 | |||||
タイプ | journal article | |||||
出版タイプ | ||||||
出版タイプ | VoR | |||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
ISSN | ||||||
収録物識別子タイプ | PISSN | |||||
収録物識別子 | 09108009 | |||||
書誌情報 |
ja : 構造工学論文集 巻 52A, p. 803-812, 発行日 2006-03 |
|||||
フォーマット | ||||||
application/pdf | ||||||
著者版フラグ | ||||||
値 | publisher | |||||
URI | ||||||
識別子 | http://hdl.handle.net/2237/7469 | |||||
識別子タイプ | HDL |