高強度GFRPのモードII層間はく離疲労き裂進展におよぼす応力比の影響
http://hdl.handle.net/2237/9159
http://hdl.handle.net/2237/915941fa0fbf-9fbd-48d6-b14f-eceb98e59360
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
JsMecEngA_70-692-580.pdf (1.4 MB)
|
|
| Item type | 学術雑誌論文 / Journal Article(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2007-12-14 | |||||
| タイトル | ||||||
| タイトル | 高強度GFRPのモードII層間はく離疲労き裂進展におよぼす応力比の影響 | |||||
| 言語 | ja | |||||
| その他のタイトル | ||||||
| その他のタイトル | Effect of Stress Ratio on Growth Behavior of Mode II Interlaminar Fatigue Cracks in High Strength GFRP | |||||
| 言語 | en | |||||
| 著者 |
松原, 剛
× 松原, 剛× MATSUBARA, Go× 尾野, 英夫× ONO, Hideo× 田中, 啓介× TANAKA, Keisuke |
|||||
| アクセス権 | ||||||
| アクセス権 | open access | |||||
| アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||
| 権利 | ||||||
| 言語 | ja | |||||
| 権利情報 | 日本機械学会 | |||||
| 権利 | ||||||
| 言語 | ja | |||||
| 権利情報 | 本文データは学協会の許諾に基づきCiNiiから複製したものである。 | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Mode II | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Fatigue | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Delamination | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | GFRP | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Stress Ratio | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Energy Release Rate | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Crack Propagation | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Interlaminar Shear | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Composite Material | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | The mode II fatigue crack growth behavior from delamination was investigated with UD laminates (made of unidirectional laminates) and C laminates (made of unidirectional laminates and cloth laminates) of high strengh glass fiber reinforced plastics (GFRP). Fatigue crack growth tests were carried out by end notched flexure speciments at the stress ratios R=0.3, 0.1, -0.5, and -1. In UD laminates, the theshold of energy release rate range, ⊿GⅡth, of fatigue crack growth was independent of the stress ratio. In C laminates, the ⊿GⅡth value at negative stress ratios was about four times of that at positive stress ratios. In C laminates, a fatigue crack propagated along the interface of the unidirectional laminate at positive stress ratios, while along the interface of the cloth cloth laminate at negative stress ratios. When the stress ratio was negative, the fracture surface of C laminates was rough because of the resin rich area of fabric crossing, and this roughness shielded the crack tip, restricting the shearing deformation near the crack tip. Thus the crack growth resistance of C laminates at negative stress ratios in much larger than that at positive stress ratios. | |||||
| 言語 | en | |||||
| 出版者 | ||||||
| 出版者 | 日本機械学会 | |||||
| 言語 | ja | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | journal article | |||||
| 出版タイプ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
| 関連情報 | ||||||
| 関連タイプ | isVersionOf | |||||
| 識別子タイプ | URI | |||||
| 関連識別子 | http://ci.nii.ac.jp/naid/110004998724/ | |||||
| ISSN | ||||||
| 収録物識別子タイプ | PISSN | |||||
| 収録物識別子 | 0387-5008 | |||||
| 書誌情報 |
ja : 日本機械学會論文集 A編 巻 70, 号 692, p. 580-587, 発行日 2004-04 |
|||||
| フォーマット | ||||||
| 値 | application/pdf | |||||
| 著者版フラグ | ||||||
| 値 | publisher | |||||
| URI | ||||||
| 識別子 | http://hdl.handle.net/2237/9159 | |||||
| 識別子タイプ | HDL | |||||