{"_buckets": {"deposit": "70ef901f-7044-4e3b-9b89-6870fdae62a5"}, "_deposit": {"id": "3897", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "3897"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00003897", "sets": ["503"]}, "author_link": ["9890", "9891", "9892", "9893"], "item_10_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2005-06", "bibliographicIssueDateType": "Issued"}, "bibliographicPageEnd": "1674", "bibliographicPageStart": "1669", "bibliographicVolumeNumber": "2", "bibliographic_titles": [{"bibliographic_title": "4th International Conference on Advances in Steel Structures, Shanghai, China,13-15 June, 2005", "bibliographic_titleLang": "en"}]}]}, "item_10_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "This study examined an accelerated corrosion test to examine corrosion degradation of coating systems for steel bridges. Three types of organic coating systems called as A-, C-, and I-painting systems in Japan and four types of metallic coating systems, zinc hop-dip galvanizing, zinc-aluminum alloy spraying by two methods and aluminum spraying, were considered. Scribe circles reaching steel substrate were made mechanically on the coated steel plates, and corrosion from them was focused. Test specimens were exposed to the accelerated corrosion environments conforming to Japanese Industrial Standards K5621 during 300 days for the metal-coated specimens and 400 days for the painted specimens. From the appearance change with passage of testing time, anticorrosive performance of the coating systems was discussed. The corrosion degradation curves for the painted specimens were presented based on blistering area of painting films.", "subitem_description_language": "en", "subitem_description_type": "Abstract"}]}, "item_10_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/5327"}]}, "item_10_select_15": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_10_text_14": {"attribute_name": "フォーマット", "attribute_value_mlt": [{"subitem_text_value": "application/pdf"}]}, "item_1615787544753": {"attribute_name": "出版タイプ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "open access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_abf2"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "金, 仁泰", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "9890", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Kim, In-Tae", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "9891", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "伊藤, 義人", "creatorNameLang": "ja"}], "nameIdentifiers": [{"nameIdentifier": "9892", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Itoh, Yoshito", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "9893", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-19"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "C-86_An_acceleration-cyclic_corrosion_test_of_coating_systems_for_steel_bridges.pdf", "filesize": [{"value": "463.6 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_note", "mimetype": "application/pdf", "size": 463600.0, "url": {"label": "C-86_An_acceleration-cyclic_corrosion_test_of_coating_systems_for_steel_bridges.pdf", "objectType": "fulltext", "url": "https://nagoya.repo.nii.ac.jp/record/3897/files/C-86_An_acceleration-cyclic_corrosion_test_of_coating_systems_for_steel_bridges.pdf"}, "version_id": "94236f1c-3c56-4fb6-8b5c-1cfbaca26956"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Steel structure", "subitem_subject_scheme": "Other"}, {"subitem_subject": "corrosion", "subitem_subject_scheme": "Other"}, {"subitem_subject": "coating system", "subitem_subject_scheme": "Other"}, {"subitem_subject": "accelerated cyclic corrosion test", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges", "subitem_title_language": "en"}]}, "item_type_id": "10", "owner": "1", "path": ["503"], "permalink_uri": "http://hdl.handle.net/2237/5327", "pubdate": {"attribute_name": "PubDate", "attribute_value": "2006-01-25"}, "publish_date": "2006-01-25", "publish_status": "0", "recid": "3897", "relation": {}, "relation_version_is_last": true, "title": ["An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges"], "weko_shared_id": -1}
  1. B200 工学部/工学研究科
  2. B200e 会議資料
  3. 国際会議

An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges

http://hdl.handle.net/2237/5327
http://hdl.handle.net/2237/5327
13734587-7298-40c4-a5bc-83b7b50ace84
名前 / ファイル ライセンス アクション
C-86_An_acceleration-cyclic_corrosion_test_of_coating_systems_for_steel_bridges.pdf C-86_An_acceleration-cyclic_corrosion_test_of_coating_systems_for_steel_bridges.pdf (463.6 kB)
Item type 学術雑誌論文 / Journal Article(1)
公開日 2006-01-25
タイトル
タイトル An Acceleration-Cyclic Corrosion Test of Coating Systems for Steel Bridges
言語 en
著者 金, 仁泰

× 金, 仁泰

WEKO 9890

ja 金, 仁泰

Search repository
Kim, In-Tae

× Kim, In-Tae

WEKO 9891

en Kim, In-Tae

Search repository
伊藤, 義人

× 伊藤, 義人

WEKO 9892

ja 伊藤, 義人

Search repository
Itoh, Yoshito

× Itoh, Yoshito

WEKO 9893

en Itoh, Yoshito

Search repository
アクセス権
アクセス権 open access
アクセス権URI http://purl.org/coar/access_right/c_abf2
キーワード
主題Scheme Other
主題 Steel structure
キーワード
主題Scheme Other
主題 corrosion
キーワード
主題Scheme Other
主題 coating system
キーワード
主題Scheme Other
主題 accelerated cyclic corrosion test
抄録
内容記述 This study examined an accelerated corrosion test to examine corrosion degradation of coating systems for steel bridges. Three types of organic coating systems called as A-, C-, and I-painting systems in Japan and four types of metallic coating systems, zinc hop-dip galvanizing, zinc-aluminum alloy spraying by two methods and aluminum spraying, were considered. Scribe circles reaching steel substrate were made mechanically on the coated steel plates, and corrosion from them was focused. Test specimens were exposed to the accelerated corrosion environments conforming to Japanese Industrial Standards K5621 during 300 days for the metal-coated specimens and 400 days for the painted specimens. From the appearance change with passage of testing time, anticorrosive performance of the coating systems was discussed. The corrosion degradation curves for the painted specimens were presented based on blistering area of painting films.
言語 en
内容記述タイプ Abstract
言語
言語 eng
資源タイプ
資源タイプresource http://purl.org/coar/resource_type/c_6501
タイプ journal article
出版タイプ
出版タイプ VoR
出版タイプResource http://purl.org/coar/version/c_970fb48d4fbd8a85
書誌情報 en : 4th International Conference on Advances in Steel Structures, Shanghai, China,13-15 June, 2005

巻 2, p. 1669-1674, 発行日 2005-06
フォーマット
application/pdf
著者版フラグ
値 publisher
URI
識別子 http://hdl.handle.net/2237/5327
識別子タイプ HDL
戻る
0
views
See details
Views

Versions

Ver.1 2021-03-01 20:50:06.203505
Show All versions

Share

Mendeley Twitter Facebook Print Addthis

Cite as

エクスポート

OAI-PMH
  • OAI-PMH JPCOAR
  • OAI-PMH DublinCore
  • OAI-PMH DDI
Other Formats
  • JSON
  • BIBTEX

Confirm


Powered by WEKO3


Powered by WEKO3