{"_buckets": {"deposit": "24bd31e2-0ccf-4e5e-9398-0e771e4627ad"}, "_deposit": {"id": "7472", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "7472"}, "status": "published"}, "_oai": {"id": "oai:nagoya.repo.nii.ac.jp:00007472"}, "item_10_alternative_title_19": {"attribute_name": "\u305d\u306e\u4ed6\u306e\u8a00\u8a9e\u306e\u30bf\u30a4\u30c8\u30eb", "attribute_value_mlt": [{"subitem_alternative_title": "J-Integral Approach to Fatigue Crack Propagation in Vulcanized Natural Rubber"}]}, "item_10_biblio_info_6": {"attribute_name": "\u66f8\u8a8c\u60c5\u5831", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2003-04", "bibliographicIssueDateType": "Issued"}, "bibliographicIssueNumber": "680", "bibliographicPageEnd": "765", "bibliographicPageStart": "758", "bibliographicVolumeNumber": "69", "bibliographic_titles": [{"bibliographic_title": "\u65e5\u672c\u6a5f\u68b0\u5b66\u6703\u8ad6\u6587\u96c6 A\u7de8"}]}]}, "item_10_description_4": {"attribute_name": "\u6284\u9332", "attribute_value_mlt": [{"subitem_description": "Fatigue tests of vulcanized natural rubber were conducted under displacement-controlled conditions. The specimens were of three types: smooth specimen, specimen with an artifical surface defect of 0.2 mm in diameter, and specimen with an artifical through-thickness defect of 2 mm in length. In smooth specimens, a fatigue crack started from natural defects of about 0.15 mm in size, and grew as an internal crack, and then became a through-thickness crack. The spring constant of the specimen decreased slowly in the range of about 80\uff05 of the total life (Stage A), followed by a rapid decrease (Stage B). The transition from Stage A to B took place when a crack penetrated through the thickness. The rate of fatigue crack propagation is expressed as a second-power function of the J-integral range both for surface cracks and through-thickness cracks. The J-integral was evaluated from the crack-center opening displacement.", "subitem_description_type": "Abstract"}]}, "item_10_identifier_60": {"attribute_name": "URI", "attribute_value_mlt": [{"subitem_identifier_type": "HDL", "subitem_identifier_uri": "http://hdl.handle.net/2237/9154"}]}, "item_10_publisher_32": {"attribute_name": "\u51fa\u7248\u8005", "attribute_value_mlt": [{"subitem_publisher": "\u65e5\u672c\u6a5f\u68b0\u5b66\u4f1a"}]}, "item_10_relation_43": {"attribute_name": "\u7570\u7248\u3067\u3042\u308b", "attribute_value_mlt": [{"subitem_relation_type": "isVersionOf", "subitem_relation_type_id": {"subitem_relation_type_id_text": "http://ci.nii.ac.jp/naid/110002370370/", "subitem_relation_type_select": "URI"}}]}, "item_10_rights_12": {"attribute_name": "\u6a29\u5229", "attribute_value_mlt": [{"subitem_rights": "\u65e5\u672c\u6a5f\u68b0\u5b66\u4f1a"}, {"subitem_rights": "\u672c\u6587\u30c7\u30fc\u30bf\u306f\u5b66\u5354\u4f1a\u306e\u8a31\u8afe\u306b\u57fa\u3065\u304dCiNii\u304b\u3089\u8907\u88fd\u3057\u305f\u3082\u306e\u3067\u3042\u308b\u3002"}]}, "item_10_select_15": {"attribute_name": "\u8457\u8005\u7248\u30d5\u30e9\u30b0", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_10_source_id_7": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "0387-5008", "subitem_source_identifier_type": "ISSN"}]}, "item_10_text_14": {"attribute_name": "\u30d5\u30a9\u30fc\u30de\u30c3\u30c8", "attribute_value_mlt": [{"subitem_text_value": "application/pdf"}]}, "item_creator": {"attribute_name": "\u8457\u8005", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "\u7530\u4e2d, \u5553\u4ecb"}], "nameIdentifiers": [{"nameIdentifier": "20960", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "TANAKA, Keisuke"}], "nameIdentifiers": [{"nameIdentifier": "20961", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "\u79cb\u5ead, \u7fa9\u660e"}], "nameIdentifiers": [{"nameIdentifier": "20962", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "AKINIWA, Yoshiaki"}], "nameIdentifiers": [{"nameIdentifier": "20963", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "\u4f86\u6d77, \u535a\u592e"}], "nameIdentifiers": [{"nameIdentifier": "20964", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "KIMACHI, Hirohisa"}], "nameIdentifiers": [{"nameIdentifier": "20965", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "\u4f0a\u85e4, \u548c\u4e4b"}], "nameIdentifiers": [{"nameIdentifier": "20966", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "ITOH, Kazuyuki"}], "nameIdentifiers": [{"nameIdentifier": "20967", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "\u30d5\u30a1\u30a4\u30eb\u60c5\u5831", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2018-02-19"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "JsMecEngA_69-680-758.pdf", "filesize": [{"value": "1.1 MB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_free", "mimetype": "application/pdf", "size": 1100000.0, "url": {"label": "JsMecEngA_69-680-758.pdf", "url": "https://nagoya.repo.nii.ac.jp/record/7472/files/JsMecEngA_69-680-758.pdf"}, "version_id": "8fd1fabf-d688-4aeb-8c3e-566b650c67aa"}]}, "item_keyword": {"attribute_name": "\u30ad\u30fc\u30ef\u30fc\u30c9", "attribute_value_mlt": [{"subitem_subject": "Fatigue Crack Propagation", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Fracture Mechanics", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Rubber", "subitem_subject_scheme": "Other"}, {"subitem_subject": "J Integral", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Smooth Specimen", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Natural Defect", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Artificial Surface Defect", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Through-thickness Crack", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "\u8a00\u8a9e", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "\u8cc7\u6e90\u30bf\u30a4\u30d7", "attribute_value_mlt": [{"resourcetype": "journal article", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "\u9632\u632f\u30b4\u30e0\u6750\u6599\u306b\u304a\u3051\u308b\u75b2\u52b4\u304d\u88c2\u9032\u5c55\u6319\u52d5\u3078\u306eJ \u7a4d\u5206\u306e\u9069\u7528", "item_titles": {"attribute_name": "\u30bf\u30a4\u30c8\u30eb", "attribute_value_mlt": [{"subitem_title": "\u9632\u632f\u30b4\u30e0\u6750\u6599\u306b\u304a\u3051\u308b\u75b2\u52b4\u304d\u88c2\u9032\u5c55\u6319\u52d5\u3078\u306eJ \u7a4d\u5206\u306e\u9069\u7528"}]}, "item_type_id": "10", "owner": "1", "path": ["320/321/322"], "permalink_uri": "http://hdl.handle.net/2237/9154", "pubdate": {"attribute_name": "\u516c\u958b\u65e5", "attribute_value": "2007-12-14"}, "publish_date": "2007-12-14", "publish_status": "0", "recid": "7472", "relation": {}, "relation_version_is_last": true, "title": ["\u9632\u632f\u30b4\u30e0\u6750\u6599\u306b\u304a\u3051\u308b\u75b2\u52b4\u304d\u88c2\u9032\u5c55\u6319\u52d5\u3078\u306eJ \u7a4d\u5206\u306e\u9069\u7528"], "weko_shared_id": 3}
防振ゴム材料における疲労き裂進展挙動へのJ 積分の適用
http://hdl.handle.net/2237/9154
543da3b7-ba44-457a-9add-50631916a0b7
名前 / ファイル | ライセンス | アクション | |
---|---|---|---|
![]() |
|
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2007-12-14 | |||||
タイトル | ||||||
タイトル | 防振ゴム材料における疲労き裂進展挙動へのJ 積分の適用 | |||||
その他のタイトル | ||||||
その他のタイトル | J-Integral Approach to Fatigue Crack Propagation in Vulcanized Natural Rubber | |||||
著者 |
田中, 啓介
× 田中, 啓介× TANAKA, Keisuke× 秋庭, 義明× AKINIWA, Yoshiaki× 來海, 博央× KIMACHI, Hirohisa× 伊藤, 和之× ITOH, Kazuyuki |
|||||
権利 | ||||||
権利情報 | 日本機械学会 | |||||
権利 | ||||||
権利情報 | 本文データは学協会の許諾に基づきCiNiiから複製したものである。 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Fatigue Crack Propagation | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Fracture Mechanics | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Rubber | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | J Integral | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Smooth Specimen | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Natural Defect | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Artificial Surface Defect | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Through-thickness Crack | |||||
抄録 | ||||||
内容記述 | Fatigue tests of vulcanized natural rubber were conducted under displacement-controlled conditions. The specimens were of three types: smooth specimen, specimen with an artifical surface defect of 0.2 mm in diameter, and specimen with an artifical through-thickness defect of 2 mm in length. In smooth specimens, a fatigue crack started from natural defects of about 0.15 mm in size, and grew as an internal crack, and then became a through-thickness crack. The spring constant of the specimen decreased slowly in the range of about 80% of the total life (Stage A), followed by a rapid decrease (Stage B). The transition from Stage A to B took place when a crack penetrated through the thickness. The rate of fatigue crack propagation is expressed as a second-power function of the J-integral range both for surface cracks and through-thickness cracks. The J-integral was evaluated from the crack-center opening displacement. | |||||
内容記述タイプ | Abstract | |||||
出版者 | ||||||
出版者 | 日本機械学会 | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源タイプresource | http://purl.org/coar/resource_type/c_6501 | |||||
タイプ | journal article | |||||
関連情報 | ||||||
関連タイプ | isVersionOf | |||||
関連識別子 | ||||||
識別子タイプ | URI | |||||
関連識別子 | http://ci.nii.ac.jp/naid/110002370370/ | |||||
ISSN | ||||||
収録物識別子タイプ | ISSN | |||||
収録物識別子 | 0387-5008 | |||||
書誌情報 |
日本機械学會論文集 A編 巻 69, 号 680, p. 758-765, 発行日 2003-04 |
|||||
フォーマット | ||||||
application/pdf | ||||||
著者版フラグ | ||||||
値 | publisher | |||||
URI | ||||||
識別子 | http://hdl.handle.net/2237/9154 | |||||
識別子タイプ | HDL |